Semiconductor device and method for fabricating the same

ABSTRACT

A semiconductor device comprises: a lower contact electrode  1;  an adhesion improving layer  3  formed on the lower contact electrode  1;  and a capacitor including a lower electrode  4  in a projected structure formed on the adhesion improving layer  3,  a capacitor dielectric film  5  formed on the lower electrode  4,  and an upper electrode  6  formed on the capacitor dielectric film  5,  in which a gap is formed on a sidewall of the adhesion improving layer  3.  The gap is at least partially left as a cavity  7.  The gap insulates the upper electrode  6  and the adhesion improving layer  3  by the cavity  7.

BACKGROUND OF THE INVENTION

The present invention relates to a semiconductor device and a method forfabricating the semiconductor device, more specifically to asemiconductor device characterized by a junction structure between anadhesion improving layer and a capacitor dielectric film used in astorage capacitor formed in a DRAM (Dynamic Random Access Memory) or anFeRAM (Ferroelectric RAM), and a method for fabricating the same.

Recently, as semiconductor devices are more highly integrated and havelarger capacities, design rules (line/space) have become increasinglyprecise. Accordingly, the semiconductor devices, e.g., DRAMs (DynamicRandom Access Memories) have widths of the wiring layers decreased, andthe contact plugs connecting the storage nodes which are to be the lowerconnection electrodes of the storage capacitors to the source regionshave smaller diameters.

Such the DRAM comprises cell regions each including one transistor andone storage capacitor, for storing 1-bit information. The storagecapacitor comprises a lower electrode called a storage node, an upperelectrode called a cell plate, and a capacitor dielectric filmsandwiched between the upper and the lower electrodes.

In the conventional DRAM, an electrode material of the storage node andthe cell plate is doped polycrystalline silicon, and the capacitordielectric film is ON film (a composite film of SiO₂ and Si₃N₄) formedby thermally oxidizing the surface of a thin CVD nitride film.

The storage node is formed in a projected electrode structure to use asa capacitor not only the upper surface but also the side surfaces,whereby a sufficient capacitance can be obtained for a limited space(floor area). This has a background that the capacitance cannot belowered below a prescribed capacitance, e.g., about 30 fF in order tocope with alpha radiation and decrease of the source voltage.

In addition, DRAMs have been developed with the integration improved byabout 4 times every three years, i.e., the micronization improved; theprojected structure of the storage capacitor, i.e., the projectedstructure of the storage node tends to become higher and higher so thata sufficient surface area can be ensured for a decreased capacitor floorarea.

However, as the storage capacitor structure becomes higher, a heightdifference from the peripheral circuit region becomes larger. Thisresultantly causes a problem that the wiring layer becomes thin at thestep, and the wiring becomes less reliable, and, in the exposing step, aproblem of a depth of focus that the higher region and the lower regioncannot be simultaneously focused.

On the other hand, although the above-described problems can be solvedby planarizing with an insulation film to be equalized the height withthe higher surface, there occur additional problems that contact holesin the peripheral circuit regions become deeper, making the etchingdifficult and that the contact holes of such high aspect ratio cannot befilled with a metal electrode material of low resistance.

Then, a material having a higher dielectric constant, i.e., a highdielectric constant film is required in place of the conventional ONfilm (a composite film of SiO₂ and Si₃N₄) as the capacitor dielectricfilm. Such the high dielectric constant film is used to thereby obtain ahigher capacitance per a unit area. Studies of obtaining a requiredcapacitance without increasing a height of the projected structure ofthe storage capacitor are made. This produces an advantage ofsimplifying steps of the fabrication.

As such the high dielectric constant film, the use of Ta₂O₅ film, SBT(SrBi₂Ta₂O₉) film, BST ((Ba,Sr)TiO₃) film, etc. are studied. These highdielectric constant materials are basically oxides, and have a problemthat when these films are deprived of oxygen, these films becomeconductive, and leak current tends to flow in the films.

DRAMs store information in charges stored in the storage capacitors.Seriously, increase of leak current means extinction of informationstored in the DRAMS.

The storage node and the cell plate of the conventional storagecapacitor are formed of polycrystalline silicon. Polycrystalline siliconcan be easily deprived of oxygen. In using a high dielectric constantfilm as the capacitor dielectric film, it is vital to use an electrodematerial which take place of polycrystalline silicon.

An electrode material suitable for such the high dielectric constantfilm must satisfy the following (1) to (6) requirements:

(1) Oxygen defect which is a cause for depriving a high dielectricconstant film of oxygen to cause leak current does not take place.

(2) An electrode material itself does not diffuse in the high dielectricconstant film to cause deterioration of the high dielectric constantfilm.

(3) An electrode material is able to withstand high-temperatureannealing for crystallizing the high dielectric constant film.

(4) The electrode material can be easily etched.

(5) An electrode material has a resistance as low as possible.

(6) An electrode material has good adhesion with a base insulation film,so that peeling does not take place after heat treatment.

However, it is very difficult to satisfy all the six requirements from(1) to (6), and no electrode material which satisfy all of therequirements has been so far found. Electrode materials, for example, Ru(Ruthenium) and RuO (Ruthenium Oxide), can satisfy, to some extent, therequirements (1) to (5) but does not satisfy the requirement (6).

That is, a Ru film and a RuO film have a defect that they tend to peelfrom the insulation film.

Then, in order to solve such defect of the peeling of these electrodefilms, which is their only one defect, it is considered to provide belowsuch electrode materials an adhesion improving layer having goodadhesion with the base insulation film for the prevention of the pealingof the electrode materials. As such the adhesion improving layer, TiN,WN, and Ta, etc. are prospective.

Here, with reference to FIGS. 38A and 38B, the storage capacitor of theconventional DRAM using Ru as the storage node and having the adhesionimproving layer will be explained.

FIG. 38B is a plan view of the DRAM at the time that a lower plug 75 ofthe DRAM is formed. FIG. 38A is a sectional view of the DRAM. In FIG.38A, the layer structure up to a first inter-layer insulation film 69 isa sectional view along the one-dot chain line B-B′ in FIG. 38B, thelayer structure from a second inter-layer insulation film 72 to a thirdinter-layer insulation film 74 is a sectional view along the one-dotline A-A′ in FIG. 38B, and the layer structure thereabove is a sectionalview again along the one-dot chain line B-B′ in FIG. 38B. In FIG. 38A,the layer structure below the third inter-layer insulation film isrepresented conveniently by A-A′ to simplify the showing.

In FIG. 38A, for convenience, a bit line 73 is shown, shorted to thelower plug 75, but they are positionally isolated from each other asshown in FIG. 38B.

Reference will be made to FIGS. 38A and 38B.

First, a device isolation oxide film 62 is formed by selective oxidationin a prescribed region of a p-type silicon substrate 61. Then, theexposed surface of the p-type silicon substrate 61 surrounded by thedevice isolation oxide film 62 is thermally oxidized to form a gateoxide film 63. Next, a non-doped polycrystalline silicon film isdeposited, and an impurity, such as P (phosphorus) or others, ision-implanted. Then, the polycrystalline silicon layer is etched into aprescribed pattern to form gate electrodes 64 and word lines 65, whichare extensions of the gate electrodes 64.

Actually, an SiO₂ film or an Si₃N₄ film as a protection film is providedby CVD method on the gate electrodes 64.

Then, as the gate electrodes 64 as a mask, an impurity, such as As(arsenic), P or others, is ion-implanted to form an n⁺-type drain region67 and an n⁺-type source region 68. Then, an SiO₂ film is deposited onthe entire surface by CVD method and is subjected to anisotropic etchingto form sidewalls 66.

Instead, in the above-described ion implanting step, As ions areimplanted to form an LDD (Lightly Doped Drain) in a shallow n⁻-typeregion, and the sidewalls 66 are formed. Then, P ions are implanted toform the n⁺-type drain region 67 and the n⁺-type source region 68.

Then, an SiO₂ film is deposited on the entire surface by CVD method toform the first inter-layer insulation film 69. A via hole for then⁺-type drain region 67 and the n⁻-type source region 68 is formed. ATiN (titanium nitride) film to be a barrier metal and next a W(tungsten) film, etc. are deposited by CVD method or sputtering method,and are polished by CMP (Chemical Mechanical Polishing) method to formcontact plugs 70, 71 with the W film, etc. buried in.

Next, an SiO₂ film is deposited on the entire surface by CVD method toform the second inter-layer insulation film 72, and a via hole for thecontact plug 70 is formed. Then, a doped polycrystalline silicon film, aWSi₂ film, etc. are deposited on the entire surface by LPCVD (LowPressure Chemical Vapor Deposition) method and then patterned to formthe bit line 73.

Next, again an SiO₂ film is deposited on the entire surface by CVDmethod to form the third inter-layer insulation film 74, and a via holefor the contact plug 71 is formed. Then again a W film is deposited onthe entire surface by LPCVD method and polished by CMP method to formthe lower plug 75 buried in the via hole.

A TiN film and an Ru film are sequentially deposited on the entiresurface by sputtering and then etched to form the adhesion improvinglayer 76 and a storage node 77 in a projected shape. Then, again a Ta₂O₅film and an Ru film are sequentially deposited by sputtering and etchedinto a prescribed shape to form the capacitor dielectric film 78 and thecell plate 70. Thus, a basic structure of the DRAM is completed.

In this case, the storage capacitor is constituted by the storage node77, the cell plate 79, and the capacitor dielectric film 78 sandwichedby both, and is electrically connected to the n⁺-type source region 68via the adhesion improving layer 76, the lower plug 75, and to thecontact plug 71.

However, in the storage capacitor using such the adhesion improvinglayer 76, the adhesion improving layer 76, and the capacitor dielectricfilm 78 of the Ta₂O₅ film contact directly to each other at both ends ofthe adhesion improving layer 76 circled by the dotted lines. At theseends, oxygen in the Ta₂O₅ film diffuses in the TiN film forming theadhesion improving layer 76 to cause oxygen defect in the Ta₂O₅ film. Asa result, a problem of deterioration of the capacitor dielectric film 78is caused.

That is, the adhesion improving layer 76 of TiN film, etc. satisfy therequirements (4) to (6) out of the requirements (1) to (6) but does notsatisfy the requirements (1) to (3). Accordingly, there occurs theproblem that the high dielectric constant film at the sidewall of theadhesion improving layer 76 is degraded, and leak current undesirablyflows.

In order to solve this problem of deterioration of the high dielectricconstant film on the sidewall of the adhesion improving layer 76, it isconsidered to from the adhesion improving layer 76 in a buriedstructure. Such improved storage capacitor will be explained withreference to FIGS. 39A and 39B.

FIG. 39A shows a sectional view of the same part as FIG. 38A. FIG. 39A,however, omits, the structure on the side of p-type silicon substrate61, and another transistor commonly using an n⁺-type drain region 67 soas to simplify the explanation.

In FIG. 39A, the view on the right side is a view showing the positionalrelationship between a storage node 77 and the adhesion improving layer76.

Reference is made to FIG. 39A.

The structure up to the third inter-layer insulation film 74 is formedin completely the same way as in FIG. 38A. Then, a via hole arriving atthe contact plug 71 is formed and then filled with the lower plug 76 ofW film by CMP. Then, the lower plug 75 is over-etched to form a cavityin the via hole. Then, a TiN film is deposited and polished by CMPmethod to be buried as the adhesion improving layer 76 in the cavity.

Hereafter, an Ru is deposited in the same way as in FIG. 38A and isetched into a prescribed shape to form the storage node 77 in aprojected shape. Next, again, a Ta₂ O₅ film and an Ru film aresequentially deposited by sputtering method and etched into a prescribedshape to form a capacitor dielectric film 78 and a cell plate 79. Thus,a basic structure of the DRAM is completed.

In the case that the adhesion improving layer 76 is thus buried, theTa₂O₅ film forming the capacitor dielectric film 78 is kept out ofdirect contact with the adhesion improving layer 76, wherebydeterioration of the capacitor dielectric film 78 never takes place.

However, as the integration of the DRAM is improved, an alignmentallowance between the storage node 77 and the adhesion improving layer76 is so small that, in view of the alignment precision of the currentexposure systems, it is actually impossible to prevent, without failure,the adhesion improving layer 78, accordingly the lower plug 75, fromappearing beyond the storage node 77. This causes additional problems.These problems will be explained with reference to FIG. 39B.

FIG. 39B is a sectional view of the same part as FIG. 39A.

Reference is made to FIG. 39B.

As shown by the view on the right side in FIG. 39B, in the case that thelower plug 75, accordingly the adhesion improving layer 76, appearsbeyond the storage node 77, the adhesion improving layer 76 and thecapacitor dielectric film 78 contact directly to each other in the partcircled by the broken line in the view on the left side in FIG. 39B. Atthis part, the deterioration of the capacitor dielectric film 78 takesplace, causing leak current.

In addition to an area of the adhesion improving layer decreased by theburied structure, when such disalignment takes place, an area of thecontact between the adhesion improving layer 76 and the storage node 77becomes smaller, which causes an additional problem of the peeling ofthe storage node 77.

SUMMARY OF THE INVENTION

An object of the present invention is to prevent the peeling of thestorage node and occurrence of leak current even when disalignment takesplace between the lower plug and the storage node.

FIGS. 1A and 1B are views explaining a principle constitution of theinvention of the present application. With reference to FIG. 1, thepresent invention will be summarized.

FIG. 1A is an enlarged sectional view of a major part of a capacitor ina case that the disalignment between a lower connection electrode 1buried in an inter-layer insulation film 2 and a lower electrode 4,e.g., disalignment between the lower plug and the storage node, isabsent. FIG. 1B is an enlarged sectional view of the major part in acase that the disalignment is present.

Reference is made to FIGS. 1A and 1B.

(1) The semiconductor device according to the present inventioncomprises: a lower contact electrode 1; an adhesion improving layer 3formed on the lower contact electrode 1; and a capacitor including alower electrode 4 in a projected structure formed on the adhesionimproving layer 3, a capacitor dielectric film 5 formed on the lowerelectrode 4, and an upper electrode 6 formed on the capacitor dielectricfilm 5, in which a gap is formed on a sidewall of the adhesion improvinglayer 3, and at least a portion of the gap is left as a cavity 7,whereby the upper electrode 6 and the adhesion improving layer 3 areinsulated from each other by the cavity 7.

The upper electrode 6, typically the cell plate is thus insulated fromthe adhesion improving layer 3 through the cavity 7, whereby even if thecapacitor dielectric film 5 and the adhesion improving layer 3 should becontiguous, generation of leak current can be prevented. A retentiontime of information in micronized DRAMs can be much longer.

(2) In the above-described semiconductor device according to the presentinvention described above in item (1), the sidewall of the adhesionimproving layer 3 is contiguous to the capacitor dielectric film 5, andthe cavity 7 is surrounded by the capacitor dielectric film 5 and theupper electrode 6.

The upper electrode 6 and the adhesion improving layer 3 are thusinsulatively isolated from each other by the cavity 7 as shown in item(1), whereby even when the sidewall of the adhesion improving layer 3and the capacitor dielectric film 5 are contiguous to therebydeteriorate the capacitor dielectric film 5 at the contiguous part, novoltage is effectively applied to the contiguous part, and increase ofleak current can be restrained.

(3) In the semiconductor device according to the present inventiondescribed above in item (1), a part of the gap is filled with thecapacitor dielectric film 5, and the cavity 7 is formed between thesidewall of the adhesion improving layer 3 and the capacitor dielectricfilm 5.

The upper electrode 6 and the adhesion improving layer 3 are insulatedby the cavity 7 as shown in item (1), and it is possible that the gap ismade narrower, and the gap is partially filled with the capacitordielectric film 5.

(4) In the semiconductor device according to the present inventiondescribed above in item (1), a whole of the gap is the cavity 7, and thecavity 7 is formed between the sidewall of the adhesion improving layer3 and the capacitor dielectric film 5.

The upper electrode 6 and the adhesion improving layer 3 are insulatedfrom each other by the cavity 7 as shown in item (1), and it is possiblethat the gap is made narrower, and the entire gap is the cavity 7.

(5) The semiconductor device according to the present inventioncomprises: a lower contact electrode 1; an adhesion improving layer 3formed on the lower contact electrode 1; and a capacitor including alower electrode 4 in a projected structure formed on the adhesionimproving layer 3, a capacitor dielectric film 5 formed on the lowerelectrode 4, and an upper electrode 6 formed on the capacitor dielectricfilm 5, in which a gap is formed on a sidewall of the adhesion improvinglayer 3, and the gap is completely filled with the capacitor dielectricfilm 5.

When the gap is thus completely filled with the capacitor dielectricfilm 5, a voltage V is applied through the buried capacitor dielectricfilm 5 of a thickness D, whereby an electric field E (=V/D) is muchmitigated, and no leak current does increase even at the contiguous partwhere the adhesion improving layer 3 and the capacitor dielectric film 5are contiguous to each other.

(6) The semiconductor device according to the present inventioncomprises: a lower contact electrode 1; an adhesion improving layer 3formed on the lower contact electrode 1; and a capacitor including alower electrode 4 in a projected structure formed on the adhesionimproving layer 3, a capacitor dielectric film 5 formed on the lowerelectrode 4, and an upper electrode 6 formed on the capacitor dielectricfilm 5, in which a gap is formed on a sidewall of the adhesion improvinglayer 3, and the gap is completely filled with an insulation film whichis different from the capacitor dielectric film 5.

In the case that the gap is thus completely filled with a depositedinsulation film, such as CVD-SiO₂ film or others, a voltage V is appliedthrough the buried capacitor dielectric film 5 of a thickness D, wherebyan electric field E (=V/D) is much mitigated. Furthermore, the adhesionimproving layer 3 and the capacitor dielectric film 5 are not contiguousdirectly to each other, whereby the capacitor dielectric film 5 does notdeteriorate.

(7) The semiconductor device according to the present inventioncomprises: a lower contact electrode 1; an adhesion improving layer 3formed on the lower contact electrode 1; and a capacitor including alower electrode 4 in a projected structure formed on the adhesionimproving layer 3, a capacitor dielectric film 5 formed on the lowerelectrode 4, and an upper electrode 6 formed on the capacitor dielectricfilm 5, in which a gap is formed on a sidewall of the adhesion improvinglayer 3, and the gap is completely filled with a self-oxidized film or aself-nitridized film of the lower electrode 4.

In this case, an self-oxide film or a self-nitride film of the lowerelectrode must be conductive.

Also in the case the gap is thus completely filled with a self-oxidefilm or a self-nitride film of the lower electrode 4, a voltage V isapplied through the thick self-oxide or self-nitride film of a thicknessD, whereby an electric field E (=V/D) is much mitigated. In addition,the adhesion improving layer 3 and the capacitor dielectric film 5 arenot contiguous directly to each other, whereby the capacitor dielectricfilm 5 does not deteriorate.

(8) The semiconductor device according to the present inventioncomprises: a lower contact electrode 1; an adhesion improving layer 3formed on the lower contact electrode 1; and a capacitor including alower electrode 4 in a projected structure formed on the adhesionimproving layer 3, a capacitor dielectric film 5 formed on the lowerelectrode 4, and an upper electrode 6 formed on the capacitor dielectricfilm 5, in which a self-oxidized film of the adhesion improving layer 3is formed on the sidewall of the adhesion improving layer 3, whereby theadhesion improving layer 3 and the capacitor dielectric film 5 areisolated from each other by the self-oxidized film of the adhesionimproving layer 3.

A self-oxide film of the adhesion improving layer is thus provided onthe sidewall of the adhesion improving layer 3, and the adhesionimproving layer 3 and the capacitor dielectric film 5 are not contiguousdirectly to each other, whereby the capacitor dielectric film does notdeteriorate. In addition, an electric filed is mitigated by an thicknessof the self-oxide film of the adhesion improving layer 3. In this case,it is not necessary to define the gap on the sidewall of the adhesionimproving layer 3.

(9) The semiconductor device according to the present inventioncomprises: a lower contact electrode 1; a capacitor including a lowerelectrode 4 in a projected structure formed on the lower contactelectrode 1, a capacitor dielectric film 5 formed on the lower electrode4, and an upper electrode 6 formed on the capacitor dielectric film 5;and an adhesion improving layer 3 being contiguous to the lowerelectrode 4 and the lower contact electrode 1, in which the adhesionimproving layer 3 is formed, covering at least a sidewall of the lowercontact electrode 1, a gap is formed on a sidewall of the adhesionimproving layer 3 at a part where the lower electrode 4 and the lowercontact electrode 1 do not disalign with each other, a gap is formed onthe sidewall of the lower contact electrode 1 at a portion of a partwhere the lower electrode 4 and the lower contact electrode 1 disalignwith each other, and each said gaps is left partially as a cavity 7,whereby the upper electrode 6 and the adhesion improving layer 3 areinsulated from each other by the cavity 7.

At least the side surface of the lower contact electrode 1 is thuscovered with the adhesion improving layer 3, whereby peeling of thelower contact electrode 1 can be effectively prevented. This leads tothe prevention of peeling of the lower electrode 4. In this case aswell, the upper electrode 6 and the adhesion improving layer 3 areinsulated from each other by the cavity 7, whereby generation of leakcurrent can be prevented.

(10) In the semiconductor device according to the present inventiondescribed above in item (9), the adhesion improving layer 3 and acapacitor dielectric film 5 are contiguous to each other, and the cavity7 is surrounded by the capacitor dielectric film 5 and the upperelectrode 6.

(11) In the semiconductor device according to the present inventiondescribed above in item (9), the gap is partially filled with thecapacitor dielectric film 5, and the cavity 7 is formed between theadhesion improving layer 3 and the capacitor dielectric film 5.

(12) In the semiconductor device according to the present inventiondescribed above in item (10), a whole of the gap is the cavity 7, andthe cavity 7 is formed between the adhesion improving layer 3 and thecapacitor dielectric film 5.

(13) The semiconductor device according to the present inventioncomprises: a lower contact electrode 1; a capacitor including a lowerelectrode 4 in a projected structure formed on the lower contactelectrode 1, a capacitor dielectric film 5 formed on the lower electrode4, and an upper electrode 6 formed on the capacitor dielectric film 5;and an adhesion improving layer 3 being contiguous to a lower electrode4 and a lower contact electrode 1, in which the adhesion improving layer3 is formed, covering at least a sidewall of the lower contact electrode1, a gap is formed on a sidewall of the adhesion improving layer 3 at apart where the lower electrode 4 and the lower contact electrode 1 donot disalign with each other, a gap is formed on a sidewall of the lowercontact electrode 1 at a portion of a part where the lower electrode 4and the lower contact electrode 1 disalign with each other, and eachsaid gaps is completely filled with a capacitor dielectric film 5.

(14) The semiconductor device according to the present inventioncomprises: a lower contact electrode 1; a capacitor including a lowerelectrode 4 in a projected structure formed on the lower contactelectrode 1, a capacitor dielectric film 5 formed on the lower electrode4, and an upper electrode 6 formed on the capacitor dielectric film 5;and an adhesion improving layer 3 being contiguous to a lower electrode4 and a lower contact electrode 1, in which the adhesion improving layer3 is formed, covering at least a sidewall of the lower contact electrode1, a gap is formed on a sidewall of the adhesion improving layer 3 at apart where the lower electrode 4 and the lower contact electrode 1 donot disalign with each other, a gap is formed on a sidewall of the lowercontact electrode 1 at a portion of a part where the lower electrode 4and the lower contact electrode 1 disalign with each other, and eachsaid gaps is completely filled with an insulation film which isdifferent form the capacitor dielectric film 5.

(15) The semiconductor device according to the present inventioncomprises: a lower contact electrode 1; a capacitor including a lowerelectrode 4 in a projected structure formed on the lower contactelectrode 1, a capacitor dielectric film 5 formed on the lower electrode4, and an upper electrode 6 formed on the capacitor dielectric film 5;and an adhesion improving layer 3 being contiguous to a lower electrode4 and a lower contact electrode 1, in which the adhesion improving layer3 is formed, covering at least a sidewall of the lower contact electrode1, a gap is formed on a sidewall of the adhesion improving layer 3 at apart where the lower electrode 4 and the lower contact electrode 1 donot disalign with each other, a gap is formed on a sidewall of the lowercontact electrode 1 at a portion of a part where the lower electrode 4and the lower contact electrode 1 disalign with each other, and eachsaid gaps is completely filled with a self-oxidized film or aself-nitridized film of the lower electrode 4.

In the semiconductor device according to the present invention describedabove in items (10) to (15), the gap is defined on the sidewall of thelower contact electrode 1 at a portion of a part where the lowerelectrode 4 and the lower contact electrode 1 disaligned from eachother. The gap is longitudinally defined. In this case as well,generation of leak current can be prevented by using the sameconstitution as stated in items (2) to (7).

(16) The semiconductor device according to the present inventioncomprises: a lower contact electrode 1; a capacitor including a lowerelectrode 4 in a projected structure formed on the lower contactelectrode 1, a capacitor dielectric film 5 formed on the lower electrode4, and an upper electrode 6 formed on the capacitor dielectric film 5;and an adhesion improving layer 3 being contiguous to a lower electrode4 and a lower contact electrode 1, in which the adhesion improving layer3 is formed, covering at least a sidewall of the lower contact electrode1, a self-oxidized film of the adhesion improving layer is formed on asidewall of the adhesion improving layer 3 at a part where the lowerelectrode 4 and the lower contact electrode 1 do not disalign with eachother, and a self-oxidized film of the adhesion improving layer 3 isformed on a exposed portion of the adhesion improving layer 3 at aportion of a part where the lower electrode 4 and the lower contactelectrode 1 disalign with each other, whereby the adhesion improvinglayer 3 and the capacitor dielectric film 5 are isolated from each otherby the self-oxidized film of the adhesion improving layer 3.

Also in the case that at least the side surface of the lower contactelectrode 1 is thus covered with the adhesion improving layer 3, anself-oxide film of the adhesion improving layer 3 is provided withoutdefining the gap to thereby prevent generation of leak current.

(17) In the semiconductor device according to the present inventiondescribed above in any one of items (9) to (16), the lower contactelectrode 1 and the lower electrode 4 are formed in one-piece with eachother.

In the case that at least the side surface of the lower contactelectrode 1 is thus covered with the adhesion improving layer 3, thelower contact electrode 1 and the lower electrode 4 may be formed inone-piece with each other. The step of forming an electrode material forburying the lower contact electrode 1, and the CMP step are notnecessary.

The semiconductor device according to the present invention comprises: alower contact electrode; a capacitor including a lower electrode in aprojected structure formed on the lower contact electrode, a capacitordielectric film formed on the lower electrode, and an upper electrodeformed on the capacitor dielectric film; and an adhesion improving layerbeing contiguous to a lower electrode and a lower contact electrode, inwhich the adhesion improving layer is formed, covering at least asidewall of the lower contact electrode, a gap is formed on a sidewallof the adhesion improving layer at a part where the lower electrode andthe lower contact electrode do not disalign with each other, and a gapis formed on a sidewall of the lower contact electrode at a portion of apart where the lower electrode and the lower contact electrode disalignwith each other.

In the above-described semiconductor device, it is preferable that eachsaid gaps is completely filled with an insulation film which isdifferent form the capacitor dielectric film.

In the above-described semiconductor device, it is preferable that eachsaid gaps is completely filled with a self-oxidized film or aself-nitridized film of the lower electrode.

The semiconductor device according to the present invention comprises: alower contact electrode; a capacitor including a lower electrode in aprojected structure formed on the lower contact electrode, a capacitordielectric film formed on the lower electrode, and an upper electrodeformed on the capacitor dielectric film; and an adhesion improving layerbeing contiguous to a lower electrode and a lower contact electrode, inwhich the adhesion improving layer is formed, covering at least asidewall of the lower contact electrode, a self-oxidized film of theadhesion improving layer is formed on a sidewall of the adhesionimproving layer at a part where the lower electrode and the lowercontact electrode do not disalign with each other, and a self-oxidizedfilm of the adhesion improving layer is formed on a exposed portion ofthe adhesion improving layer at a portion of a part where the lowerelectrode and the lower contact electrode disalign with each other,whereby the adhesion improving layer and the capacitor dielectric filmare isolated from each other by the self-oxidized film of the adhesionimproving layer.

(18) The method for fabricating the semiconductor device according tothe present invention includes the step of etching an adhesion improvinglayer 3 which is contiguous to a lower electrode 4 of a capacitor in aprojected structure and a lower contact electrode 1, in which theadhesion improving layer 3 is excessively etched to form a gap, and thena capacitor dielectric film 5 covering the lower electrode 4 is formed.

The gap for insulating the upper electrode 6 and the adhesion improvinglayer 3 from each other can be formed simply and by self-alignment byexcessively etching the adhesion improving layer 3.

(19) In the method for fabricating the semiconductor device according tothe present invention described above in item (18), the adhesionimproving layer 3 is formed to cover at least a sidewall of the lowercontact electrode 1, a gap is formed on a sidewall of the adhesionimproving layer 3 at a part where the lower electrode 4 and the lowercontact electrode 1 disalign with each other, and a gap is formed on thesidewall of the lower contact electrode 1 at a portion of a part wherethe lower electrode 4 and the lower contact electrode 1 disalign witheach other.

In the case that to prevent peeling of the lower contact electrode 1,the adhesion improving layer 3 is thus provided to cover at least theside surface of the lower contact electrode 1, the gap is defined on thesidewall of the lower contact electrode 1 at a portion of a part wherethe lower electrode 4 and the lower contact electrode 1 disaligned fromeach other, which makes no problem.

(20) The semiconductor device fabrication method according to thepresent invention comprises the steps of: forming an opening in aninsulation film; forming an adhesion improving layer 3, covering atleast a sidewall of the opening; depositing a conductive material,filling the opening; polishing or etching back the conductive materialto form the lower contact electrode 1 and a lower electrode 4 buried inthe opening, the lower contact electrode 1 and the lower electrode 4being formed in one-piece; removing at least a part of the insulationfilm; etching the exposed adhesion improving layer 3 to form a gap on asidewall of the lower contact electrode 1; and forming a capacitordielectric film 5 covering the lower electrode 4.

The lower contact electrode 1 and the lower electrode 4 may be thusformed unseparable in one-piece by CMP. In this case as well, theadhesion improving layer 3 is excessively etched to define byself-alignment the gap on the sidewall of the lower contact electrode 1.

(21) The semiconductor device fabrication method according to thepresent invention comprises the steps of: etching an adhesion improvinglayer 3 contiguous to a lower electrode 4 of a capacitor in a projectedstructure and a lower contact electrode 1; oxidizing at least an exposedpart of the adhesion improving layer 3 to form a self-oxidized film ofthe adhesion improving layer 3; and forming a capacitor dielectric film5 covering the lower electrode 4.

In the case that a self-oxide film of the adhesion improving layer 3 isthus used, the excessive etching step for defining the gap isunnecessary. The steps can be simple.

(22) In the semiconductor device fabrication method according to thepresent invention described in item (21), the adhesion improving layer 3is formed so as to cover at lest a sidewall of the lower contactelectrode 1.

The adhesion improving layer 3 is thus provided to cover at least theside surface of the lower contact electrode 1, whereby peeling of thelower contact electrode 1 can be prevented, which leads to theprevention of peeling of the lower electrode 4.

(23) The semiconductor device fabrication method according to thepresent invention comprises the steps of: forming an opening in aninsulation film; forming an adhesion improving layer 3, covering atleast a sidewall of the opening; depositing a conductive material,filling the opening; polishing or etching back the conductive materialto form a lower contact electrode 1 and a lower electrode 4 buried inthe opening, the lower contact electrode 1 and the lower electrode 4being formed in one-piece; removing at least a part of the insulationfilm; etching an exposed portion of the adhesion improving layer 3;oxidizing the exposed portion of the adhesion improving layer 3; andforming a capacitor dielectric film 5 covering the lower electrode 4.

In the case that the lower contact electrode 1 and the lower electrode 4are thus formed unseparable in one-piece by CMP, a self-oxide film ofthe adhesion improving layer 3 is used, whereby the excessive etchingstep for defining the gap is unnecessary. The steps can be simple.

(24) In the semiconductor device fabrication method according to thepresent invention described in any one of items (18) to (23), aprotection film is formed on the upper surface of the lower electrode 4,and an upper electrode 6 covering a sidewall of the lower electrode 4 isformed by depositing a conductive material and anisotropically etchingthe conductive material with the protection film as a mask.

It is possible that the protection film is provided on the upper surfaceof the lower electrode 4 in a projected shape through the adhesionimproving layer 3, and anisotropic etching is performed with theprotection film as a mask to form the upper electrode 6 forming thecapacitor as, e.g., a sidewall-like electrode on the sidewall of thelower electrode 4. This is effective especially in a case that becauseof high integration the etching of the upper electrode 6 is difficult.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A and 1B are views explaining the principle constitution of thepresent invention.

FIGS. 2A-2B are views explaining those of the fabrication steps offabricating the semiconductor device according to a first embodiment ofthe present invention, which are on the way to the completion of thesemiconductor device.

FIGS. 3A-3B are views explaining those of the fabrication steps offabricating the semiconductor device according to the first embodimentof the present invention, which follow the last one of the steps shownin FIGS. 2A and 2B and are on the way to the completion of thesemiconductor device.

FIGS. 4A-4B are views explaining those of the fabrication steps offabricating the semiconductor device according to the first embodimentof the present invention, which follow the last one of the steps shownin FIG. 3B.

FIGS. 5A-5B are enlarged views of a major part of the first embodimentof the present invention.

FIG. 6 is a view explaining a modification of the first embodiment ofthe present invention.

FIGS. 7A-7B are views explaining a major part of a second embodiment ofthe present invention.

FIGS. 8A-8B are enlarged views of a major part of a third embodiment ofthe present invention.

FIGS. 9A-9B are enlarged views of a major part of a fourth embodiment ofthe present invention.

FIGS. 10A-10B are views explaining those of the fabrication steps offabricating the semiconductor device according to a fifth embodiment ofthe present invention, which are on the way to the completion of thesemiconductor device.

FIGS. 11A-11B are views of those of the fabrication steps of fabricatingthe semiconductor device according to the fifth embodiment of thepresent invention, which follow the last one of the steps shown in FIG.10B.

FIGS. 12A-12C are views explaining those of the fabrications steps offabricating the semiconductor device according to a sixth embodiment ofthe present invention, which are on the way to the completion of thesemiconductor device.

FIGS. 13A-13B are views explaining those of the fabrication steps of thesemiconductor device according to the sixth embodiment of the presentinvention, which follow the last one of the steps shown in FIG. 12C.

FIGS. 14A-14B are views explaining those of the fabrication steps of thesemiconductor device according to a seventh embodiment of the presentinvention, which are on the way to the completion of the semiconductordevice.

FIGS. 15A-15B are views explaining those of the fabrication steps offabricating the semiconductor device according to the seventh embodimentof the present invention, which follow the last one of the steps shownin FIG. 14B.

FIGS. 16A-16B are views explaining those of the fabrication steps offabricating the semiconductor device according to an eighth embodimentof the present invention, which are on way to the completion of thesemiconductor device.

FIGS. 17A-17B are views explaining those of the fabrication steps offabricating the semiconductor device according to the eighth embodimentof the present invention, which follows the last one of the fabricationsteps shown in FIG. 16B.

FIGS. 18A-18B are enlarged views of a major part of the semiconductordevice according to the eighth embodiment of the present invention.

FIGS. 19A-19B are enlarged views of a major part of the semiconductordevice according to a ninth embodiment of the present invention.

FIGS. 20A-20B are enlarged views of a major part of the semiconductordevice according to a tenth embodiment of the present invention.

FIGS. 21A-21B are enlarged views of a major part of the semiconductordevice according to an eleventh embodiment of the present invention.

FIGS. 22A-22B are enlarged views of a major part of the semiconductordevice according to a twelfth embodiment of the present invention.

FIGS. 23A-23B are enlarged views of a major part of the semiconductordevice according to a thirteenth embodiment of the present invention.

FIGS. 24A-24B are enlarged views of a major part of the semiconductordevice according to a fourteenth embodiment of the present invention.

FIGS. 25A-25B are views explaining the fabrication steps for fabricatingthe semiconductor device according to a fifteenth embodiment of thepresent invention.

FIGS. 26A-26B are views explaining those of the fabrication steps offabricating the semiconductor device according to a sixteenth embodimentof the present invention, which are on the way to the completion of thesemiconductor device.

FIGS. 27A-27B are views explaining those of the fabrication steps offabricating the semiconductor device according to the sixteenthembodiment of the present invention, which follow the last one of thefabrication steps shown in FIG. 26B and are on the way to the completionof the semiconductor device.

FIGS. 28A-28B are views explaining those of the fabrication steps offabricating the semiconductor device according to the sixteenthembodiment of the present invention, which follow the last one of thefabrication steps shown in FIGS. 27A and 27B and are on the way to thecompletion of the semiconductor device.

FIGS. 29A-29B are views explaining those of the fabrication steps offabricating the semiconductor device according to the sixteenthembodiment of the present invention, which follow the last one of thefabrication steps shown in FIGS. 28A and 28B and are on the way to thecompletion of the semiconductor device.

FIGS. 30A and 30B are views explaining those of the fabrication steps offabricating the semiconductor device according to the sixteenthembodiment of the present invention, which follow the last one of thefabrication steps shown in FIGS. 29A and 29B and are on the way to thecompletion of the semiconductor device.

FIGS. 31A and 31B are views explaining those of the fabrication steps offabricating the semiconductor device according to the sixteenthembodiment of the present invention, which follow the last one of thefabrication steps shown in FIGS. 30A and 30B.

FIG. 32 is a view explaining a modification of the eighth embodiment ofthe present invention.

FIGS. 33A and 33B are views explaining a modification of the sixteenthembodiment of the present invention.

FIGS. 34A-34C and 35A-35B are views explaining a modification of theeighth embodiment of the present invention.

FIGS. 36A-36C and 37A-37B are views explaining a modification of thesixteenth embodiment of the present invention.

FIGS. 38A and 38B are views explaining the storage capacitor of theconventional DRAM.

FIGS. 39A and 39B are views explaining a structure and problems of theimproved storage capacitor of the conventional DRAM.

DETAILED DESCRIPTION OF THE INVENTION A First Embodiment

A first embodiment of the present invention will be explained withreference to FIGS. 2A-2B, 3A-3B, 4A-4B and 5A-5B.

FIG. 2B is a plan view of a DRAM at the time that a lower plug 25 isformed. FIG. 2A is a sectional view of the DRAM. In FIG. 2A, the layerstructure of the DRAM below a first inter-layer insulation film 19including the first inter-layer insulation film 19 corresponds to thatof the sectional view along the one-dot chain line B-B′ in FIG. 2B, thelayer structure of the DRAM of a second inter-layer insulation film 22to a third inter-layer insulation film 24 corresponds to that of thesectional view along the one-dot chain line A-A′ in FIG. 2B, and thelayer structure of the DRAM above the third inter-layer insulation film24 excluding the third inter-layer insulation film 24 corresponds tothat of the sectional view along the one-dot chain line B-B′ in FIG. 2B.In FIG. 2A, etc., to simplify the showing, a layer structure of the DRAMup to the third inter-layer insulation film 24 including the inter-layerinsulation film 24 is represented by A-A′.

In FIG. 2A, etc., a bit line 23 is shorted to the lower plug 25 forconvenience of the showing, but actually they are positionally isolatedfrom each other as shown in FIG. 2B.

Reference is made to FIGS. 2A and 2B.

First, a device isolation oxide film 12 is formed by selective oxidationin a prescribed region of a p-type silicon substrate 11, and then theexposed surface of the p-type silicon substrate 11 surrounded by thedevice isolation oxide film 12 is thermally oxidized to form a gateoxide film 13. Then, a non-doped polycrystalline silicon layer isdeposited, then is doped with P (phosphorus) ions and next etched into aprescribed pattern to form gate electrodes 14 and word lines 15, whichare extensions of the gate electrodes 14.

Actually, an SiO₂ film or an Si₃N₄ film as a protection film is providedon the gate electrodes 14 by CVD method.

Next, with the gate electrodes 14 as a mask, As (arsenic) ions areimplanted to form an n⁺-type drain region 17 and an n⁺-type sourceregion 18. Then, an SiO₂ film is deposited on the entire surface by CVDmethod and etched to form sidewalls 16.

In the above-described ion-implanting step, instead it is possible thatan LDD (Lightly Doped Drain) region of a shallow n⁻-type region isformed, and As ions are implanted after the sidewalls 16 have beenformed, to form the n⁺-type drain region 17 and the n⁺-type sourceregion 18.

Next, again an SiO₂ film is deposited on the entire surface by CVDmethod to form the first inter-layer insulation film 19, and then viaholes for the n⁺-type drain region 17 and the n⁺-type source region 18are formed. Then a TiN film and a W film to be a barrier metal issequentially deposited by sputtering method and polished by CMP methodto form contact plugs 20, 21 with the TiN film, the W, etc. buried in.

An SiN film to be a stopper in the CMP step may be formed on the firstinter-layer insulation film 19.

Then again, an SiO₂ film is deposited on the entire surface by CVDmethod to form the second inter-layer insulation film 22, and then a viahole for the contact plug 20 is formed. Then, a doped polycrystallinesilicon film is deposited on the entire surface by LPCVD method andpatterned to form the bit line 23.

Next again, an SiO₂ film is deposited on the entire surface by CVDmethod to form the third inter-layer insulation film 24, and then a viahole arriving at the contact plug 21 is formed. Then, an Ru film isdeposited on the entire surface by CVD method which is superior in stepcoverage and polished by CMP method to form the lower plug 25 buried inthe via hole. In this specification, the lower plug (the lower contactelectrode) means a electrode which is electrically contiguous to thelower portion of the storage node (the lower electrode). The lowerelectrode may be formed also on the side portion of the bit line or onthe upper portion of the bit line.

It is also possible to provide on the third inter-layer insulation film24 an SiN film to be the stopper in the CMP step.

Reference is made to FIG. 3A.

Next, a TiN film 26 of a 1-100 nm-thick, e.g., a 10 nm-thick, isdeposited on the entire surface by sputtering method, and again an Rufilm 27 of, e.g., a 1.0 μm-thick is deposited by CVD method.

Reference is made to FIG. 3B.

Then, the Ru film is etched by anisotropic etching using a prescribedetching mask and an O₂+Cl₂ mixed gas into a-prescribed pattern which is,for example, 0.25 μm-width along the bit line 23 and 0.5 μm-width alongthe word lines so as to form a projected storage node 29.

The TiN film 26 is not substantially etched by the O₂+Cl₂ mixed gas, andcan function as the etching stopper.

Next, the exposed portion of the TiN film 26 is etched isotropic etchingusing heated hydrochloric acid, sulfuric acid, hydrogen peroxide aqueoussolution+hydrochloric acid, or hydrogen peroxide aqueoussolution+sulfuric acid, and then the TiN film 26 is excessively etchedto form an adhesion improving layer 28 defining a slit-shaped gap on thesidewall.

Incidentally, a height of the gap is a film thickness “d” of theadhesion improving layer 28.

The etching is not essentially wet etching, and may be dry etching aslong as the etching is isotropic.

Reference is made to FIG. 4A.

Then, a Ta₂O₅ film 30 of a thickness ″d_(ε)” of , e.g., 10 nm-thick, andan Ru film 31 of, e.g., a 150 nm-thick are sequentially deposited by CVDmethod.

Reference is made to FIG. 4B.

Next, the Ru film 31 and the Ta₂O₅ film 30 are sequentially etched intoa prescribed shape to form a cell plate 33 and a capacitor dielectricfilm 32.

Reference is made to FIG. 5A.

FIG. 5A is an enlarged view of the major part circled by the dotted linein FIG. 4B. In the above-described case, a height of the gap, i.e., athickness “d” of the adhesion improving layer 28 satisfies therelationship2×d _(ε) <d≦d _(v)with respect to a thickness d_(ε) of the capacitor dielectric film 32and a width d_(v) which permits the CVD-Ru film forming the cell plate33 to intrude capably of the step coverage. As a result, the capacitordielectric film 32 of Ta₂O₅ intrudes deep into the gap to becomecontiguous to the sidewall of the adhesion improving layer 28, while theCVD-Ru film, which is good but inferior to Ta₂O₅ in the step coverage,intrudes into the gap up to the vicinity of the entrance of the gap toform the cell plate 33. Thus, the gap is partially surrounded by thecapacitor dielectric film 32 and the cell plate 33 to form a cavity 34.

The capacitor dielectric film 32 has the film quality deteriorated atthe contiguous portion between the adhesion improving layer 28 and thecapacitor dielectric film 32. However, a voltage is applied to thecontiguous portion through the cavity 34. Accordingly, the adhesionimproving layer 28 and the cell plate 33 are isolated from each other,effectively insulated from each other by the cavity 34, and no leakcurrent flows. Accordingly, a charge stored in the capacitor can besufficiently retained.

Reference is made to FIG. 5B.

FIG. 5B is an enlarged view of the major part for explaining thedisalignment between the storage node 29 and the lower plug 25. As inFIG. 5A, the capacitor dielectric film 32 of Ta₂O₅ intrudes deep intothe gap to become contiguous to the sidewall of the adhesion improvinglayer 28, while the CVD-Ru film, which is good but inferior to Ta₂O₅ inthe step coverage, intrudes into the gap up to the vicinity of theentrance of the gap to form the cell plate 33. Thus, the gap ispartially surrounded by the capacitor dielectric film 32 and the cellplate 33 to form the cavity 34.

In a case that the cell plate 33 is deposited by sputtering method, thestep coverage is inferior, and a width d_(v) becomes larger.

In this case, even when the disalignment takes place, the storage node29 is contiguous to the adhesion improving layer 28 at the samecontiguous area as is when the disalignment does not take place andnever peel.

In this case, a capacitor is formed also between the lower plug 25 andthe cell plate 33.

As described above, in the present embodiment, the adhesion improvinglayer 28 is excessively etched to define the slit-shaped gap, and a partof the gap is formed in the cavity 34. Even when the adhesion improvinglayer 28 and the capacitor dielectric film are contiguous to each other,the cavity 34 effectively insulates the adhesion improving layer 28 fromthe cell plate 33. Accordingly, leak current does not flow.

Even when the disalignment takes place between the storage node 29 andthe lower plug 25, the storage node 29 is contiguous to the adhesionimproving layer 28 at the same contiguous area as is when thedisalignment does not take place to be thereby maintained stable. Thestorage node 29 never peels.

In this case, a capacitor is formed also between the lower plug 25 andthe cell plate 33.

A Modification of the First Embodiment

Then, with reference to FIG. 6, a modification of the first embodimentof the present invention will be explained.

Reference is made to FIG. 6.

FIG. 6 is a sectional view of the modification in the same state as FIG.4B. The deposition steps up to the Ru film depositing step including theRu film depositing step are completely the same as those of the firstembodiment. The explanation of the steps up to the Ru film depositingstep including the Ru film depositing step will be omitted.

In the same way as in the first embodiment, an Ru film is deposited,then a TiN film to be an adhesion improving layer of, e.g., a 10nm-thick is deposited by sputtering method. Next, a 300 nm-thick SiNfilm to be a protection film is formed by CVD method. Then theprotection film, the TiN film, the Ru film, and the TiN film are etchedinto the same shape as in the first embodiment to form an insulationfilm 36, the adhesion improving layer 35 and the storage node 29. Next,the adhesion improving layers 28, 35 are excessively etched to define aslit-shaped gap.

The adhesion improving layer 35 is side-etched, but there is no problem.

Then, a Ta₂O₅ film and a Ru film are deposited and then areanisotropically etched by reactive ion etching with the insulation film36 as a mask to form sidewall-shaped cell plate 33 and a capacitordielectric film 32.

In the modification of the first embodiment, the cell plate 33 is thusformed by anisotropical etching in a sidewall shape by self-alignment,which permits the photolithography step to be omitted, and furthermoreis effective in a case that, because of high integration, for the usuallithography step, the storage nodes 29 are too high, and a gap betweenthe storage nodes 29 is too small.

A Second Embodiment

Next, a second embodiment of the present invention will be explainedwith reference to FIGS. 7A and 7B.

Reference is made to FIGS. 7A and 7B.

FIGS. 7A and 7B correspond to FIGS. 5A and 5B. The sequence of thefabrication steps, and the materials forming the respective elements arecompletely the same as those of the first embodiment, and theexplanation of the fabrication steps is omitted.

In the second embodiment, a thickness “d” of the adhesion improvinglayer 28 of TiN film is below 20 nm, e.g., 10 nm, a depth of the gap,i.e., an excessive etched amount of the adhesion improving layer 28 is10-20 nm, and Ta₂O₅ film forming the capacitor dielectric film 32 isdeposited in a 10 nm-thick, filling completely the gap with the Ta₂O₅film forming the capacitor dielectric film 32.

That is, in the second embodiment, the relationshipd≦2×d _(ε)is satisfied.

In the second embodiment as well, the capacitor dielectric film 32 iscontiguous to the sidewall of the adhesion improving layer 28, but theadhesion improving layer 28 and the cell plate 33 are isolated from eachother by the capacitor dielectric film 32 of a thickness of (a depth ofthe gap+a film thickness d_(ε) of the capacitor dielectric film)≈2×d_(ε)˜3×d _(ε). An applied electric field is mitigated, and leak current doesnot flow.

When the disalignment takes place between the storage node 29 and thelower plug 25 as shown in FIG. 7B, the storage node 29 is contiguous tothe adhesion improving layer 28 at the same contiguous area as in thecase that the disalignment does not take place, whereby the storage node29 is maintained stable and never peels.

A Third Embodiment

Then, a third embodiment of the present invention will be explained.

Reference is made to FIGS. 8A and 8B.

FIGS. 8A and 8B correspond to FIGS. 5A and 5B. The sequence of thefabrication steps, and the materials forming the respective elements arecompletely the same as those of the first embodiment, and theexplanation of the fabrication steps is omitted.

In the third embodiment, a film thickness “d” of the adhesion improvinglayer 28 of TiN film is as thin as 1-10 nm. In a case that Ta₂O₅ filmforming the capacitor dielectric film 32 is deposited in a 10 nm-thick,even CVD-Ta₂O₅ film, which is superior in the step coverage, cannotintrude deep into the gap, and the cavity 34 is formed between theadhesion improving layer 28 and the capacitor dielectric film 32.

In the third embodiment, the capacitor dielectric film 32 is notcontiguous to the sidewall of the adhesion improving layer 28, wherebythe capacitor dielectric film 32 does not deteriorate.

The adhesion improving layer 28 is isolated from the cell plate 33 bythe cavity 34 and the relatively thick capacitor dielectric film 32,whereby an applied electric field is mitigated, and leak current doesnot flow.

In this case as well, when the disalignment takes place between thestorage node 29 and the lower plug 25 as shown in FIG. 8B, the storagenode 29 is contiguous to the adhesion improving layer 28 at the samecontiguous area as in the case that the disalignment does not takeplace, whereby the storage node 29 can be maintained stable and neverpeels.

A Fourth Embodiment

Next, a fourth embodiment of the present invention will be explainedwith reference to FIGS. 9A and 9B.

Reference is made to FIGS. 9A and 9B.

FIGS. 9A and 9B correspond to FIGS. 5A and 5B. The sequence of thefabrication steps, and the materials forming the respective elements arecompletely the same as those of the first embodiment, and theexplanation of the fabrication steps is omitted.

In the fourth embodiment, a thickness “d” of the adhesion improvinglayer of TiN film is further thinned to below 5 nm. In a case that Ta₂O₅film is deposited in a 10 nm-thick, even CVD-Ta₂O₅ film cannotsubstantially into the gap, and the entire gap becomes the cavity 34.

In the fourth embodiment as well, the capacitor dielectric film 32 isnot contiguous to the sidewall of the adhesion improving layer 28,whereby the capacitor dielectric film 32 does not deteriorate. Theadhesion improving layer 28 and the cell plate 33 are isolated from eachother by the long cavity 34, whereby an applied electric field ismitigated, and leak current does not flow.

In a case that the storage node 29 is disaligned with the lower plug 25as shown in FIG. 9B, the storage node 29 is contiguous to the adhesionimproving layer 28 at the same contiguous area as in the case that thestorage node 29 is not disaligned and maintained stable. The storagenode 29 does not peel.

When the capacitor dielectric film 32 is formed by sputtering method orCVD method using a high pressure or a high temperature for forming thefilm, the step coverage can be much degraded, whereby even in a casethat a height of the gap, i.e., a thickness d of the adhesion improvinglayer 28 is as thick as above 5 nm, the capacitor dielectric film 32 canhave the same film state as in FIGS. 9A and 9B.

A Fifth Embodiment

Then, a fifth embodiment of the present invention will be explained withreference to FIGS. 10A-10B and 11A-11B.

FIGS. 10A, 10B and 11A are enlarged views of the contiguous portionbetween the lower plug 25 and the storage node 29 and correspond to FIG.5A. FIG. 11B corresponds to FIG. 5B.

The fabrication steps up to the step of excessively etching the adhesionimproving layer 28 including the adhesion improving layer excessiveetching step are completely the same as those of the first embodiment,and the explanation of these steps is omitted.

Reference is made to FIG. 10A.

The adhesion improving layer 28 is formed by performing the completelythe same excessive etching as in the first embodiment.

Reference is made to FIG. 10B.

Then, the surface of the storage node 20 of Ru film is oxidized by aheat-treatment in an oxidizing atmosphere of 450-600° C. to form aruthenium oxide (RuO) film 38, so that the gap on the sidewall of theadhesion improving layer 28 is filled with the ruthenium oxide film 38owing to volume expansion of the Ru (ruthenium) at the time of itstransform to the ruthenium oxide.

That is, the heat-treatment is performed for a period of time in whichthe gap on the sidewall of the adhesion improving layer 28 is completelyfilled with the ruthenium oxide film 38.

The exposed portion of the sidewall of the adhesion improving layer 28is oxidized, and oxide film 37 is formed.

Reference is made to FIG. 11A.

After the above-described step, a Ta₂O₅ film and an Ru are deposited inthe same way as in the first embodiment and are etched into a prescribedshape to form the capacitor dielectric film 32 and the cell plate 33.Thus, a basic structure of the DRAM is completed.

Reference is made to FIG. 11B.

In a case that the disalignment takes place between the storage node 29and the lower plug 25, in the step of oxidizing the storage node 29 theexposed portion of the Ru film forming the lower plug 25 is alsooxidized to form an RuO film.

The ruthenium oxide film 38, which has good conductivity, does notdecrease a capacitance and, in addition, satisfies the above-describedrequirements (1) to (5), and accordingly does not deteriorate the filmquality of capacitor dielectric film 32.

In the fifth embodiment, the capacitor dielectric film 32 and theadhesion improving layer 28 are not contiguous to each other, wherebydeterioration of the capacitor dielectric film 32 does not take place.

In the description of the fifth embodiment, the self-oxidized film isused, but the storage node may be nitridized to bury the gap with aself-nitridized film. In this case, the self-nitridized film must haveconductivity, and accordingly the storage node 29 must be formed of aconductive member whose self-nitridized film has conductivity. Forexample, it is possible that W is used in place of Ru, and aself-nitridized film (WN film) having conductivity formed by nitridizingthe surface of the W film is used.

In this case, in which, as shown in FIG. 11B, the disalignment takesplace between the storage node 29 and the lower plug 25, the storagenode 29 is contiguous to the adhesion improving player 28 at the samecontiguous area as in the case that the disalignment does not takeplace, whereby the storage node 29 does not peel.

A Sixth Embodiment

Next, the fabrication steps of a sixth embodiment of the presentinvention will be explained with reference to FIGS. 12A-12C and 13A-13B.

FIGS. 12A-12C and 13A are enlarged views of the major part of thecontiguous portion between the lower plug 25 and the storage node 29 andcorrespond to FIG. 5A. FIG. 13B corresponds to FIG. 5B.

The fabrication steps up to the step of excessively etching the adhesionimproving layer 28 including the adhesion improving layer 28 arecompletely the same as those of the first embodiment, and theexplanation of these steps is omitted.

Reference is made to FIG. 12A.

The excessive etching is performed in completely the same way as in thefirst embodiment to form the adhesion improving layer 28.

A thickness of the adhesion improving layer 28 is 10-50 nm, e.g., 20 nm.

Reference is made to FIG. 12B.

Then, the insulation film 39 of SiO₂ film is deposited by CVD method tofill the gap with the insulation film 39.

Reference is made to FIG. 12C.

Then, the insulation film 39 deposited on the surfaces of the storagenode 29 and of the third inter-layer insulation film 24 is removed byisotropic etching, leaving the insulation film 39 only in the gap.

Reference is made to FIG. 13A.

After the above-described step, in the same way as in the firstembodiment, a Ta₂O₅ film and an Ru film are deposited and etched into aprescribed shape to form the capacitor dielectric film 32 and the cellplate 33. Thus a basic structure of the DRAM is completed.

Reference is made to FIG. 13B.

The gap is substantially completely filled with the insulation film 39at a portion where the storage node 29 is disaligned with respect to thelower plug 25.

Porosities often remain in the buried insulation film 39, but it makesno problem.

In the sixth embodiment, the capacitor dielectric film 32 and theadhesion improving layer 28 are not contiguous to each other, andaccordingly the capacitor dielectric film 32 does not deteriorate. Theinsulation film 39 of SiO₂ film is buried completely between theadhesion improving layer 28 and the cell plate 33, and the insulationfilm 39 mitigates an applied electric field, and leak current does notflow.

In a case that, as shown in FIG. 13B, the disalignment between thestorage electrode 29 and the lower plug 25 takes place, the storage node29 is contiguous to the adhesion improving layer 28 at the samecontiguous area as in the case that the disalignment does not takeplace, whereby the storage node 29 is maintained stable and does notpeel.

In the above description, the insulation film 39 filling the gap is SiO₂film, but in place of SiO₂ film, SiN film may be deposited by CVDmethod. In this case, the etching of the third inter-layer insulationfilm 24 in the isotropic etching may not be considered because SiN filmcan be selectively etched with respect to the third inter-layerinsulation film 24.

A Seventh Embodiment

Next, the fabrication steps of a seventh embodiment of the presentinvention will be explained with reference to FIGS. 14A-14B and 15A-15B.

FIGS. 14A-14B and 15A are enlarged view of the major part of thecontiguous portion between the lower plug 25 and the storage node 29 andcorresponds to FIG. 5A. FIG. 15B corresponds to FIG. 5B.

The steps up to the step of etching the adhesion improving layer 28including the adhesion improving layer etching step are completely thesame as those of the first embodiment, and the explanation of thesesteps is omitted.

Reference is made to FIG. 14A.

The adhesion improving layer 28 is formed by completely the same etchingas in the first embodiment.

The excessive etching is not performed. Accordingly the gap is notdefined on the sidewall of the adhesion improving layer 28.

Reference is made to FIG. 14B.

Then, a heat-treatment is performed in an oxidizing atmosphere of450-600° C. to oxidize the surface of the storage node 29 of Ru film soas to form a ruthenium oxide film 38 and also to oxidize the exposedsurface of the adhesion improving layer 28 to transform the TiN film tothe oxide film 37 of TiO.

Reference is made to FIG. 15A.

After the above-described step, in the same way as in the firstembodiment, a Ta₂O₅ film and an Ru film are deposited and etched into aprescribed shape to form the capacitor dielectric film 32 and the cellplate 33. Thus, a basic structure of the DRAM is completed.

Reference is made to FIG. 15B.

In a case that the disalignment between the storage node 29 and thelower plug 25 takes place, in the step of oxidizing the storage node 29the exposed portion of the Ru film forming the lower plug 25 is alsooxidized to form a ruthenium oxide film 40.

TiO is an insulator, and the adhesion improving layer 28 and the cellplate 33 are not electrically shorted with each other. The oxide film 37of TiO does not deteriorate the film quality of the capacitor dielectricfilm 32.

In the seventh embodiment, the capacitor dielectric film 32 and theadhesion improving layer 28 are not contiguous to each other. Thecapacitor dielectric film 32 does not deteriorate. The adhesionimproving layer 28 is insulated from the cell plate 33 by the oxide film37 of TiO, and accordingly leak current does not flow.

In the description of the seventh embodiment, the self-oxidized film ofthe adhesion improving layer 28 is used, but it is possible that theadhesion improving layer is nitridized to use a self-nitridized film forthe insulation. In this case, the adhesion improving layer 28 must beformed of a conductive member whose self-nitridized film hasinsulativity, and the storage node 29 must be formed of a conductivemember whose self-nitridized film has conductivity.

In a case that the disalignment between the storage node 29 and thelower plug 25 takes place as shown in FIG. 15B, the storage node 29 iscontiguous to the adhesion improving layer 28 at the same contiguousarea as in the case that the disalignment does not take place, andaccordingly maintained stable. The storage node 29 does not peel.

An Eighth Embodiment

In the first to the seventh embodiments, the lower plug 25 and theadhesion improving layer 28 are flatly contiguous to each other at thetop surface of the lower plug 25. The adhesion of the lower plug 25 isnot always sufficient. Furthermore, insufficient adhesion of the storagenode 29 can be considered. Then, with reference to FIGS. 16A-16B,17A-17B and 18A-18B, an eighth embodiment of the present invention inwhich an adhesion improving layer 43 is provided, covering at least thesides of a lower plug 42 for improved adhesion of the lower plug 42 willbe explained.

The fabrication steps up to the step of forming a via hole for a contactplug 21 including the contact plug via hole forming step are completelythe same as those of the first embodiment, and their explanation isomitted. A basic structure below a gate oxide film 13 is not shown.

Reference is made to FIG. 16A.

Following the step of forming a via hole for the contact plug 21 incompletely the same way as in the first embodiment, a TiN film 41 isdeposited on the entire surface by CVD method, covering the insidesurface of the via hole. Then, an Ru film is deposited also by CVDmethod and polished by CMP method to bury the Ru film in the via hole toform the lower plug 42. Next, again an Ru film of, e.g., a 1.0 μm-thickis deposited by CVD method.

Reference is made to FIG. 16B.

Next, in the same way as in the first embodiment, anisotropic etching isperformed using a prescribed etching mask as a mask and a O₂+Cl₂ mixedgas to etch the Ru film 27 into a prescribed shape which is, forexample, 0.25 μm-width along bit lines 23 and 0.5 μm-width along wordlines 15. Thus the storage node 29 in a projected shape is formed.

Next, the exposed portion of the TiN film 41 is isotropically etchedusing heated hydrochloric acid, sulfuric acid, hydrogen peroxide aqueoussolution+hydrochloric acid, or hydrogen peroxide aqueoussolution+sulfuric acid, and the TiN film 41 is excessively etched toform an adhesion improving layer 43 defining a slit-shaped gap on thesidewall.

The etching is not essentially wet etching, and may be dry etching aslong as the etching is isotropic.

Reference is made to FIG. 17A.

Then, in the same way as in the first embodiment, a Ta₂O₅ film 30 of athickness d_(ε) of, e.g., 10 nm, and an Ru film 31 of, e.g., a 150nm-thick are sequentially deposited by CVD method.

Reference is made to FIG. 17B.

Next, in the same way as in the first embodiment, the Ru film 31 and theTa₂O₅ film 30 are sequentially etched into a prescribed shape to form acell plate 33 and a capacitor dielectric film 32.

Reference is made to FIG. 18A.

FIG. 18A is an enlarged view of the major part circled by the dottedline in FIG. 17B and corresponds to FIG. 5A showing the firstembodiment. A height of the gap, i.e., a thickness “d” of the adhesionimproving layer 43 satisfies the relationship2×d _(ε) <d≦d _(v)with respect to a thickness d_(ε) of the capacitor dielectric film 32and a width d_(v) which permits the CVD-Ru film forming the cell plate33 to intrude capably of the step coverage. As a result, as in FIG. 5A,the capacitor dielectric film 32 of Ta₂O₅ intrudes deep into the gap tobecome contiguous to the sidewall of the adhesion improving layer 43,and the cell plate 33 also intrudes into the gaps. Thus, the gap ispartially surrounded by the capacitor dielectric film 32 and the cellplate 33 to form a cavity 34.

The capacitor dielectric film 32 has the film quality deteriorated atthe contiguous portion between the adhesion improving layer 43 and thecapacitor dielectric film 32. However, a voltage is applied to thecontiguous portion through the cavity 34. Accordingly, the adhesionimproving layer 43 and the cell plate 33 are isolated from each other,effectively insulated from each other by the cavity 34, and no leakcurrent flows. Accordingly, a charge stored in the capacitor can besufficiently retained.

Reference is made to FIG. 18B.

FIG. 18B corresponds to FIG. 5B and is an enlarged view of a major partshowing the disalignment between the storage node 29 and the lower plug42. The adhesion improving layer 43 is excessively etched on the sidewhere the disalignment has taken place, and a gap is defined along thesidewall of the lower plug 42.

The capacitor dielectric film 32 intrudes deep into the gap to becontiguous to the exposed upper surface of the adhesion improving layer43. The cell plate 33 intrudes into the gap and partially fills the gap.Thus, a cavity surrounded by the capacitor dielectric film 32 and thecell plate 33 is defined.

As described above, in the eighth embodiment of the present invention,the sidewall and the bottom surface of the lower plug 42 are coveredwith the adhesion improving layer 43, whereby the lower plug hasimproved adhesion and does not peel, which leads to improved adhesion ofthe storage node 29, and the storage node 29 does not peel either.

In the case that the disalignment between the storage node 29 and thelower plug 42 takes place, the storage node 29 and the adhesionimproving layer 43 are contiguous at a larger contiguous area, and thecavity 34 is formed by the over-etching only along the sidewall of thelower plug 42 and is not formed right below the storage node.Accordingly, the storage node 29 does not fall to peel. Another merit isthat a large margin can be allowed for the over-etching, and accordinglythe etching step does not require precise control.

In the eighth embodiment as well, a relationship among the adhesionimproving layer 43, the capacitor dielectric film 32 and the cell plate33 is substantially equal to that of the first embodiment, and leakcurrent does not flow.

A Ninth Embodiment

Next, a ninth embodiment of the present invention will be explained withreference to FIGS. 19A-19B.

Reference is made to FIGS. 19A and 19B.

FIGS. 19A and 19B correspond to FIGS. 7A and 7B. The sequence of thefabrication steps and material forming the respective members arecompletely the same as those of the eighth embodiment, and theirexplanation is omitted.

In the ninth embodiment, a thickness “d” of the adhesion improving layer43 of TiN film is below 20 nm, e.g., 10 nm, a height or a depth of thegap, i.e., an excessive etched amount of the adhesion improving layer 43is 10-20 nm. A Ta₂O₅ film forming the capacitor dielectric film 32 isdeposited in a 10 nm-thick to completely fill the gap with the Ta₂O₅film forming the capacitor dielectric film 32.

That is, in the ninth embodiment, the relationshipd≦2×d _(ε)is satisfied.

In the ninth embodiment as well, the capacitor dielectric film 32 iscontiguous to the exposed end of the adhesion improving layer 43, butthe adhesion improving layer 43 and the cell plate 33 are isolated bythe capacitor dielectric film 32 of a thickness of (a depth of the gap+athickness d_(ε))2×d_(ε)−3×d_(ε). An applied electric field is mitigated,and leak current does not flow.

A Tenth Embodiment

Then, a tenth embodiment of the present invention will be explained withreference to FIGS. 20A-20B.

Reference is made to FIGS. 20A and 20B.

FIGS. 20A and 20B correspond to FIGS. 8A and 8B. The sequence of thefabrication steps and the material forming the respective members arecompletely the same as those of the eighth embodiment, and theirexplanation will be omitted.

In the tenth embodiment, a thickness “d” of the adhesion improving layer43 of TiN film is as small as 1-10 nm. Even when Ta₂O₅ film forming thecapacitor dielectric film 32 is deposited in a 10 nm-thick, evenCVD-Ta₂O₅ film, which is superior in step coverage, cannot intrude deepinto the gap, and the cavity 34 is formed between the adhesion improvinglayer 43 and the capacitor dielectric film 32.

In the tenth embodiment as well, the capacitor dielectric film 32 is notcontiguous to the exposed end of the adhesion improving layer 43,whereby the capacitor dielectric film 32 does not deteriorate. Theadhesion improving layer 43 and the cell plate 33 are isolated by thecavity 34 and the relatively thick capacitor dielectric film 32, wherebyan applied electric field is mitigated, and leak current does not flow.

An Eleventh Embodiment

Then, with reference to FIG. 21, an eleventh embodiment of the presentinvention will be explained.

Reference is made to FIGS. 21A and 21B.

FIGS. 21A and 21B correspond to FIGS. 9A and 9B. The sequence of thefabrication steps and the material of their respective members arecompletely the same as those of the eighth embodiment, and theirexplanation will be omitted.

In the eleventh embodiment, a thickness “d” of the adhesion improvinglayer 43 is further as thin as below 5 nm. In a case that Ta₂O₅ filmforming the capacitor dielectric film 32 is deposited in a 10 nm-thick,even CVD-Ta₂O₅ film cannot substantially intrude into the gap, and theentire gap becomes the cavity 34.

In the eleventh embodiment as well, the capacitor dielectric film 32 isnot contiguous to the exposed end of the adhesion improving layer,whereby the capacitor dielectric film does not deteriorate. The adhesionimproving layer 43 and the cell plate 33 are isolated from each other bythe elongate cavity 34, whereby an applied electric field is mitigated,and leak current does not flow.

In the eleventh embodiment as well, when the capacitor dielectric film32 is formed by sputtering method or CVD method using a high pressure ora high temperature for forming the film, the step coverage can be muchdegraded, whereby even in a case that a height of the gap, i.e., athickness “d” of the adhesion improving layer 28 is as thick as above 5nm, the capacitor dielectric film 32 can have the same film state as inFIGS. 21A and 21B.

A Twelfth Embodiment

Then, a twelfth embodiment of the present invention will be explainedwith reference to FIGS. 22A-22B.

FIGS. 22A and 22B correspond to FIGS. 11A and 11B. The fabrication stepsup to the step of forming the storage node 29 including the storage nodeforming step are completely the same as those of the eighth embodiment,and the fabrication steps following the storage node forming step arethe same as those of the fifth embodiment. Their explanation will beomitted.

Reference is made to FIG. 22A.

The twelfth embodiment provides a structure which is effectivelyequivalent to that shown in FIG. 11A. A ruthenium oxide film 38 formedby oxidizing the storage node 29 completely fills the gap.

Reference is made to FIG. 22B.

On the other hand, in a case that the disalignment between the storagenode 29 and the lower plug 42 takes place, the exposed surface of the Rufilm forming the lower plug 42 is also oxidized to form ruthenium oxidefilm 38. The ruthenium oxide film formed by oxidizing the lower plug 42completely fills the gap.

In the oxidation step, the oxide film of TiO is also formed on theexposed sidewall or the exposed upper surface of the adhesion improvinglayer 43.

In the twelfth embodiment, the capacitor dielectric film 32 and theexposed portion of the adhesion improving layer 43 are isolated fromeach other, whereby the capacitor dielectric film 32 does notdeteriorate.

In the above description of the twelfth embodiment, the self-oxidizedfilm is used, but the storage node or the lower plug may be nitridizedto fill the gap with the self nitridized film. In this case, because theself-nitridized film must be conductive, it is necessary to form thestorage node 29 and the lower plug 42 are formed of conductive materialswhose nitridized films have conductivity.

A Thirteenth Embodiment

Then, a thirteenth embodiment of the present invention will be explainedwith reference to FIGS. 23A-23B.

FIGS. 23A and 23B correspond to FIGS. 13A and 13B. The fabrication stepsup to the step of forming the storage node 29 including the storage nodeforming step are completely the same as those of the eighth embodiment,and the fabrication step following the storage node forming step are thesame as those of the sixth embodiment. Their explanation will beomitted.

Reference is made to FIG. 23A.

The thirteenth embodiment also provides a structure which is effectivelyequivalent to that shown in FIG. 13A. The gap on the sidewall of theadhesion improving layer 43 is completely buried with the insulationfilm 39 of SiO₂ film.

A thickness of the adhesion improving layer 43 is 10-50 nm, e.g., 20 nm.

Reference is made to FIG. 23B.

In a case that the disalignment between the storage node 29 and thelower plug 42 takes place, the gap defined on the sidewall of thestorage node 29 is completely filled with the insulation film 39 of SiO₂film.

In the thirteenth embodiment as well as in the sixth embodiment, thecapacitor dielectric film 32 is not contiguous to the exposed end of theadhesion improving layer 43, whereby the capacitor dielectric film 32does not deteriorate. The adhesion improving layer 43 and the cell plate33 are isolated, insulated from each other by the insulation film 39,whereby an applied electric field is mitigated, and leak current doesnot flow.

In the above description of the thirteenth embodiment, the insulationfilm 39 filling the gap is SiO₂ film, but in place of SiO₂ film, SiNfilm may be deposited by CVD method. In this case, SiN film has etchingselectivity with respect to the third inter-layer insulation film 24,and the etching of the third inter-layer insulation film 24 may not beconsidered in the isotropic etching step.

A Fourteenth Embodiment

Then, a fourteenth embodiment of the present invention will be explainedwith reference to FIGS. 24A-24B.

FIGS. 24A and 24B correspond to FIGS. 15A and 15B. The fabrication stepsup to the step of forming the storage node 29 including the storage nodeforming step are completely the same as those of the eighth embodiment,and the fabrication steps following the storage node forming step arethe same as those of the seventh embodiment. Their explanation will beomitted.

Reference is made to FIG. 24A.

The fourteenth embodiment provides a structure which is effectivelyequivalent to that shown in FIG. 15A. On the sidewall of the adhesionimproving layer 43, the adhesion improving layer 43 is oxidized to formthe oxide film 44 of TiO, and the oxide film 44 isolates the adhesionimproving layer 43 and the capacitor dielectric film 32 from each other.

Reference is made to FIG. 24B.

In a case that the disalignment between the storage node 29 and thelower plug 42 takes place, the exposed upper surface of the adhesionimproving layer 43 is oxidized to form the oxide film 44 of TiO. Theoxide film 44 isolates the adhesion improving layer 43 and the capacitordielectric film 32 from each other.

Because of the TiO, which is insulative, the adhesion improving layer 43and cell plate 33 does not electrically short with each other. The oxidefilm 44 of TiO does not deteriorate film quality of the capacitordielectric film 32.

In the fourteenth embodiment as well as the seventh embodiment, thecapacitor dielectric film 32 and the sidewall of the adhesion improvinglayer are not contiguous to each other, whereby the capacitor dielectricfilm 32 does not deteriorate. The adhesion improving layer 43 and thecell plate 33 are isolated, insulated from each other by the oxide film44 of TiO, and leak current does not flow.

In the description of the fourteenth embodiment, the self-oxidized filmof the adhesion improving layer 43 is used, but it is possible that theadhesion improving layer 43 is nitridized to use the self-nitridizedfilm for the insulative isolation. In this case, the self-nitridizedfilm of the adhesion improving layer 43 must be conductive, and theself-nitridized film of the storage node 29 must be conductive.Accordingly, it is necessary that the adhesion improving layer 43 isformed of a conductive material whose self-nitridized film isinsulative, and the storage node 29 is formed of a conductive materialwhose self-nitridized film is conductive.

A Fifteenth Embodiment

Next, with reference to FIGS. 25A-25B, a fifteenth embodiment of thepresent invention which is a modification of the eighth embodiment willbe explained.

The fabrication steps up to the step of forming the via hole for thecontact plug 21, i.e., the step of depositing the TiN film 41 so as toburied in the lower plug hole 45, including the via hole forming stepare completely the same as those of the eighth embodiment of the presentinvention. Their explanation will be omitted.

Reference is made to FIG. 25A.

In completely the same way as in the eighth embodiment, a TiN film 41 isdeposited on the entire surface, and then an Ru film is deposited by CVDmethod to have a thickness of, e.g., 1.0 μm on the flat portion.

In this step, the interior of the lower plug hole 45 is completelyfilled with the Ru film 27, and the lower plug 46 is in one-piece withthe storage node 29.

Reference is made to FIG. 25B.

Following this step, in completely the same way as in the eighthembodiment, a Ta₂O₅ film of a thickness d_(ε) of 10 nm, and an Ru filmof, e.g., a 150 nm-thick are sequentially deposited and etched into aprescribed shape to form the cell plate 33 and the capacitor dielectricfilm 32.

The structure circled by the dotted line in FIG. 25B is substantiallythe same as in FIG. 18A or FIG. 18B.

In the fifteenth embodiment, the lower plug 46 and the storage node 29are formed in one-piece, whereby the number of film forming steps can bedecreased. The CMP step for burying the lower plug 46 into the lowerplug hole 45 is not necessary, which simplifies the fabrication steps.

The other characteristics of the fifteenth embodiment are the same asthose of the eighth embodiment.

The fabrication steps after the step of etching the storage node 29 ofthe fifteenth embodiment may be changed to the fabrication stepscorresponding to those of the ninth to the fourteenth embodiments. Inthis case, the same functional effects as those provided by the ninth tothe fourteenth embodiments can be provided.

A Sixteenth Embodiment

Then, with reference to FIGS. 26A-26B, 27A-27B, 28A-28B, 29A-29B,30A-30B, and 31A-31B, a sixteenth embodiment of the present inventionwill be explained.

The views on FIGS. 27A, 28A, 29A, 30A and 31A are explanatory views offorming solid rectangular pole-shaped storage node 53. The views onFIGS. 27B, 28B, 29B, 30B and 31B are explanatory views of forming hollowrectangular pole-shaped storage node 54, i.e., cylindrical storage node.

The fabrication steps up to the step of forming a bit line 23 includingthe bit line forming step are completely the same as those of the firstembodiment, and their explanation will be omitted. The substratestructure below the gate oxide film 13 is also omitted. In FIGS.27A-27B, 28A-28B, 29A-29B, 30A-30B, and 31A-31B, a transistor on theleft side which co-uses the n⁺-type drain region is omitted.

Reference is made to FIG. 26A.

In the same way as in the first embodiment, the bit line 23 is formed,then the third inter-layer insulation film 24 of SiO₂ film is deposited,next, an SiN film to be an etching stopper 47 is deposited on the entiresurface, and a thick insulation film 48 of an SiO₂ film of, e.g., a 1.0μm-thick is deposited.

An SiN film (not shown) may be formed on the entire surface, directlycovering the bit line 23. Actually in the vicinity of the contact plug21, the SiN film is formed contiguously directly on the secondinter-layer insulation film 22, and can be an etching stopper in thenext step of forming an opening.

An SiN film to be a stopper in the CMP step may be formed on theinsulation film 48.

Reference is made to FIG. 26B.

Next, anisotropic etching is performed by reactive ion etching to forman opening 49 arriving at a contact plug 21.

In this step, first an opening arriving at an etching stopper 47 isformed, and the etching stopper 47 is selectively removed. Then, thethird inter-layer insulation film 24 and the second inter-layerinsulation film 22 are removed to expose the contact plug 21.

A planar shape of the opening 49 is the rectangle having a 0.25 μm-widthalong the bit line and a 0.5 μm-width along the word lines 15. Theopening 49 is formed, offset from the bit line 23 as in the firstembodiment.

Reference is made to FIGS. 27A and 27B.

Then, a TiN film 50 is deposited on the entire surface by CVD method tocover the side surfaces and the bottom surface of the opening 49, and anRu film 51 is deposited again by CVD method. In forming the rectangularpole storage node, as shown in FIG. 27A, the opening 49 is completelyfilled with the Ru film 51. In forming the cylindrical storage node, asshown in FIG. 27B, the opening 49 is not completely filled with the Rufilm 51, leaving a concavity which contours the shape of the opening 49.

Reference is made to FIGS. 28A and 28B.

Then, the Ru film 51 and the TiN film 50 on the flat upper surface ofthe insulation film 48 are polished by CMP to form the adhesionimproving layer 52 and the storage nodes 53, 54 buried in the opening49.

The storage nodes 53, 54 are effectively the lower plugs.

Reference is made to FIGS. 29A and 29B.

Then, the insulation film 48 is selectively removed by diluted HF withthe etching stopper 47 as a stopper.

Reference is made to FIGS. 30A and 30B.

Then, the exposed portion of the adhesion improving layer 52 is etchedby wet etching using heated hydrochloric acid, sulfuric acid, hydrogenperoxide aqueous solution+hydrochloric acid, hydrogen peroxide aqueoussolution+sulfuric acid or diluted HF, and furthermore the adhesionimproving layer 52 is excessively etched to define a gap along thesidewalls of the storage nodes 53, 54.

Reference is made to FIGS. 31A and 31B.

In completely the same way as in the first embodiment, a Ta₂ O₅ film ofa thickness d_(ε) of, e.g., 10 nm and an Ru film of, e.g., a 150nm-thick are sequentially deposited by CVD method, and the Ru film andTa₂O₅ film are etched into a prescribed shape to form the cell plate 56and the capacitor dielectric film 55.

The structures circled by the dotted lines in FIGS. 31A and 31B aresubstantially the same as shown in FIG. 18B.

In the sixteenth embodiment, the parts which are substantially the lowerplugs are formed in one piece with the storage nodes 53, 54, whereby thenumber of the film forming steps can be small and the CMP step forburying the lower plugs in the lower plug holes is not necessary.Furthermore, the storage nodes 53, 54 are formed by CMP, whereby the Rufilm may not be formed thick in comparison with that in the case thatthe storage nodes are formed by etching, whereby a use amount of Ru canbe smaller.

In the sixteenth embodiment, the parts which are effectively to be thelower plugs are formed in one-piece with the storage nodes 53, 54,whereby the storage nodes 53, 54 are contiguous to the adhesionimproving layer 52 at a larger contiguous area, whereby the adhesion isimproved, and accordingly the storage nodes 53, 54 do not peel.

The other characteristics are substantially the same as those of thecase that the disalignment between the storage node and the lower plugtakes place in the eighth embodiment.

The fabrication steps following the step of etching the adhesionimproving layer 52 of the sixteenth embodiment may be changed tocorrespond to the ninth to the fourteenth embodiments, whereby the sameeffects as those produced by the ninth to the fourteenth embodiments canbe provided.

In the case that the fabrication steps following the step of etching theadhesion improving layer 52 are changed to correspond to the fourteenthembodiment, the excessive etching of the adhesion improving layer 52 isnot performed.

Embodiments of the present invention have been explained above, andother various modification of the present invention are possible. Forexample, the constitution of the variation of the first embodiment,which is shown in FIG. 6, is applicable as it is to the second to thesixteenth embodiments and their modifications.

The constitution of the modification of the first embodiment is notapplicable to the sixteenth embodiment using the cylindrical storagenode 54.

In the eighth to the sixteenth embodiments, the adhesion improving layeris contiguous to the side surfaces and bottom surface of the lower plug,but it is not essential to cover all the side surfaces and the bottomsurface of the lower plug. As shown in FIGS. 32, 33A, and 33B, theadhesion improving layer may be formed on an upper part of the sidesurfaces which is a little below a position where the cavity is formedby the over-etching.

In this case, the adhesion improving layer may be formed only on theupper surface of the third inter-layer insulation film 24, whereby theadhesion improving layer can function as a peeling prevention film.

In this case, as shown in FIGS. 34A-34C, 35A-35B, 36A-36C, and 37A-37B,the via hole for the lower plugs 25, 42 may be formed by forming theadhesion improving layer thin on the entire surface before the via holefor the lower plugs 25, 42 is formed and then etching the adhesionimproving layer and the insulation film below the adhesion improvinglayer by using a resist pattern.

Idealistically, an electrode material forming the lower plug is the samematerial as the lower electrode called the storage node, but may beformed of a material different from that of the lower electrode as longas the above-described requirements (1) to (3) are satisfied.

In the above-described respective embodiments, the capacitor dielectricfilm is a high dielectric constant film of Ta₂O₅ film, but is notlimited to Ta₂O₅ film. High dielectric constant films, such as, SBT(SrBi₂Ta₂O₉) film BST ((Ba,Sr)TiO₃) film, PZLT film etc. may be used.

In the description of the above-described respective embodiments, thecontact plugs, etc. are formed by sputtering method, but CVD method maybe used in place of sputtering method.

In the description of the above-described embodiments, the bit line isformed of doped polycrystalline silicon film, but may be formed of ametal, such as W or others, or a silicide, such as WSi, or others.

The present invention has been explained by means of the above-describedrespective embodiments in which the present invention is applied to thestorage capacitor of a DRAM. However, the present invention is notessentially applied to DRAMs, and is applicable to semiconductorintegrated circuit devices requiring a number of capacitors, especiallyto ferroelectric memories (FeRAMs) having the same structure as DRAMs,whereby FeRAMs of high integration can be fabricated.

In an application of the present invention to an FeRAM, information isstored by using residual polarization of the capacitor dielectric filmof the storage capacitor. Accordingly, the capacitor dielectric filmmust be a high dielectric constant film of a ferroelectric film, such asSBT film, PZT film or others.

In the above-described respective embodiments, the storage node, thelower plug and the cell plate are formed of Ru film, but Ru film is notessential. At least one of the storage node, the lower plug and the cellplate may be formed of ruthenium oxide (RO) film, W film, Pt (platinum)film or others.

In the above-described respective embodiments, the present invention isapplied to so-called COB (Capacitor Over Bit line) structure, which thestorage node is provided over the bit line. However, the presentinvention is not related to the bit line. Thus, the present inventionmay be also applicable to so-called CUB (Capacitor Under Bit line)structure.

In the above-described respective embodiments, the adhesion improvinglayer is formed of TiN. A conducting material, which can improveadhesion between the lower plug and the storage electrode and canselectively etch against the storage electrode and peripheral insulationfilm, may be also used as the adhesion improving layer. Thus, WN, Ti,TiAlN, W, etc. are also applicable to the adhesion improving layerinstead of TiN.

When the adhesion improving layer is formed between the storage node anda silicon layer such as an amorphous silicon or a polycrystallinesilicon, the adhesion improving layer can act also as a barrier metalwhich prevents silicidation between the storage node and the siliconlayer. In this case, TiN, WN, etc. are preferable to the adhesionimproving layer. From the point of view of the contact resistance, it ispreferable that the adhesion improving layer is formed by stacked filmof a barrier metal layer and a contact metal layer. In this case,TiN/Ti, WN/Ti, etc. may be used.

After the fabrication step shown in FIGS. 28A and 28B in the sixteenthembodiment, the adhesion improving layer 52 may be etched to form a slitbetween the insulation film 48 and the storage node 53 or 54. In thiscase, insulation film 48 is not removed but left, and then the capacitordielectric film 55 and cell plate 56 are formed to form concave-typecapacitor. In this case, slit structures, which corresponds to thestructures circled by the dotted lines in FIGS. 31A and 31B, is formedon a portion between the upper portion of the storage node 53 or 54 andthe insulation film 48.

According to the present invention, an electrode material of the storagenode is a material which does not deteriorate a high dielectric film,and the adhesion improving layer for improving adhesion of the storagenode is excessively etched or oxidized, whereby even when disalignmenttakes place between the storage node and the lower plug, generation ofleak current due to deterioration of the high dielectric constant filmcan be effectively restrained. This permits a high dielectric constantfilm to be used as the capacitor dielectric film. The present inventionmuch contributes to realization of semiconductor integrated circuitdevices of the next generation, such as DRAMs, etc. having higherintegration and higher density.

1-22. (canceled)
 23. A method for fabricating a semiconductor devicecomprising the steps of: etching an adhesion improving layer contiguousto a lower electrode of a capacitor in a projected structure and a lowercontact electrode; oxidizing at least an exposed part of the adhesionimproving layer to form a self-oxidized film of the adhesion improvinglayer; and forming a capacitor dielectric film covering the lowerelectrode.
 24. A method for fabricating a semiconductor device accordingto claim 23, wherein the adhesion improving layer is formed so as tocover at least a sidewall of the lower contact electrode. 25-27.(canceled)
 28. A method for fabricating a semiconductor device accordingto claim 23, wherein a protection film is formed on the upper surface ofthe lower electrode, and an upper electrode covering a sidewall of thelower electrode is formed by depositing a conductive material andanisotropically etching the conductive material with the protection filmas a mask.
 29. (canceled)